PELCO High Temperature Carbon Paste
Carbon flakes in an inorganic silicate solution for bonding resisting up to 2000 C.
The PELCO High Temperature Carbon Paste is aimed for applications where a conductive cement is needed which withstand temperatures up to 2000 °C (3632 °F).
This paste is ideally suited for mounting specimens on hot stages for SEM , FESEM, XPS, ESCA, SIMS and AUGER systems.
Also for applications where silver migration or a reaction with silver or nickel flakes could be a problem, this product would be an excellent alternative.
Carbon content is 50-60% by weight in an inorganic silicate aqueous solution.
Conductivity in cured state is 4.6 ohm/square/mil. Must be fully cured to achieve good conductivity and strong bond.
Soluble in water to 260 °C (500 °F).
Cure schedule is: air dry at room temperature for 2-4 hours, step cure at 93 °C (200 F) and final cure at 260 °C (500 °F).